Nai-post sa 2019-02-12Ang silicone at ang nano-powder na ginagamot sa nano-dispersion ay dispersed sa isang mayorya ng resin cross-linked polymerized composite resins, at pagkatapos na mabago, ang zinc powder at ang aluminum powder ay maaaring makuha upang magkaroon ng chromium-free, acid- lumalaban, at Magnesium alloy chromium-free Dacromet solution na may mga pakinabang ng salt spray resistance, proteksyon sa kapaligiran, manipis na coating film, magandang weather resistance at impact resistance.Zhang Shuyong et al.idinagdag ang zinc powder, aluminum powder, deionized water, dispersant (decadiol polyoxyethylene ether o cetyl polyoxyethylene ether), phosphate (aluminum hydroxide at 85% phosphoric acid sa proporsyon), Thickener (nalulusaw sa tubig na methyl cellulose ether o hydroxypropyl methyl cellulose ether), sodium tripolyphosphate, polymerization initiator (35% hydrogen peroxide at / o potassium permanganate), pH regulator (zinc oxide, oxidation Calcium o calcium hydroxide) at filming aid (polyethylene glycol) ay halo-halong ayon sa isang tiyak na ratio, hinalo nang pantay, at ang pH ay kinokontrol sa 3.5 hanggang 5.5 upang makakuha ng chromium-free na Dacromet coating liquid.Ang imbensyon ay pangkalikasan at walang polusyon.Ang pagganap ng kaagnasan ay 7 hanggang 10 beses na mas mataas kaysa sa electrogalvanized, at mayroon din itong mga pakinabang ng mataas na permeability, mataas na pagbabawas ng friction, at mataas na paglaban sa panahon.Zhu Chengfei et al.Zinc powder, aluminum powder, wetting and dispersing agent (alcohol o polyalcohol), passivating agent (phytic acid), corrosion inhibitor (sodium molybdate), tubig, film forming agent (manganese acetate, manganese nitrate o Manganese chloride), filming aid (silane). coupling agent), bumubuo ng tulong (boric acid o succinic acid) at pampalapot (hydroxymethyl cellulose o hydroxyethyl cellulose) ay inihanda ayon sa isang tiyak na ratio upang makakuha ng walang Kumpara sa naunang sining, ang chromium dacrox coating liquid ay may mga pakinabang ng walang polusyon, walang polusyon, mababang pagkonsumo ng enerhiya at mahusay na paglaban sa pagsusuot.
Gamit ang phosphoric acid bilang binder at passivating agent, ang rare earth ay auxiliary, aluminum powder, zinc powder, 85% phosphoric acid, aluminum hydroxide, hydrogen peroxide, calcium oxide, cetyl polyoxyethylene ether, hydroxypropyl cellulose ether , ammonium cerium nitrate at ammonium nitrate ay pinaghalo ayon sa isang tiyak na ratio, hinalo pantay-pantay, at ang pH ay kinokontrol sa 5.5, upang makakuha ng isang chromium-free Dacromet patong likido na may mahusay na kaagnasan pagtutol.Ang pananaliksik ay nagpapakita na ang pagdaragdag ng rare earth strontium salt ay epektibong binabawasan ang patong.Ang corrosion current ng layer ay may magandang corrosion inhibition effect sa Dacromet coating.
Oras ng post: Ene-13-2022